ULTRA- AND NANODISPERSED STRUCTURES OF THE PLASMA COATINGS STRENGTHENED BY ELECTROMECHANICAL TREATMENT

The structures of plasma coatings after electromechanical treatment (EMT) are studied by scanning probe microscopy on the example of PRFBH6-2 and R6M5 coatings. The results obtained indicate that ultra- and nanoscale strengthening phase are formed and fixed in the coating structure after EMT. The allocation of such phases at decay of the initial coating structure during rapidly high-speed temperature-force action occurs. The classification and the analysis of the formation mechanisms of coatings specific structural zones, strengthened by nano- and ultrafine particles in different ratios and defined by parameters of spray powder, regimes of plasma spraying and EMT are researched.

1. Stoica V., Ahmed R., Itsukaichi T. et. al. Sliding wear evaluation of hot isostatically pressed (HIPed) thermal spray cermet coatings. – In book: Proceedings of the 2003 International Thermal Spray Conference. – Orlando, 2003. P. 459 – 466.

2. Поварова К.Б., Бурмистров В.И., Антонова А.В. и др. // Металлы. 2006. № 3. С. 83 – 90.

3. Shaw L., Goerman D., Ren R., Gell M. // J. Surface and Coating Technology. 2000. № 130. P. 1 – 8.

4. Gell M., Jordan E.H., Sohn Y.H. et. al. // J. Surface and Coa tings Technology. 2001. № 146-147. P. 48 – 54.

5. Skandan G., Ya o R., Kear B.H. et. al. // J. Scripta Materials. 2001. № 44. P. 1699 – 1702.

6. Jordan E.H., Gell M., Shaw L., Jiang S. // J. Materials Science and Engineering. 2001. № A301. P. 80 – 89.

7. Багмутов В.П., Калита В.И., Захаров И.Н., Комлев Д.И. // Фундаментальные проблемы современного материаловедения. 2007. Т. 4. № 1. С. 18 – 23.

8. Пат. 2338005 РФ. Способ комбинированного упрочнения поверхностей деталей / В.П. Багмутов,

9. В.И. Калита, С.Н. Паршев, И.Н. Захаров // Изобретения. Полезные модели. 2008. № 31. С. 8.

10. Багмутов В.П., Калита В.И., Захаров И.Н. и др. // Изв. вуз. Черная металлургия. 2009. № 10. C. 62 – 68.

11. Калита В.И., Комлев Д.И. // Металлы. 2003. № 6. С. 30 – 37.

12. Калита В.И., Багмутов В.П., Захаров И.Н. и др. // Физика и химия обработки материалов. 2008. № 1. С. 38 – 42.

13. Багмутов В.П., Калита В.И., Захаров И.Н., Паршев С.Н. // Физика и химия обработки материалов. 2007. № 3. С. 22 – 28.

14. Калита В.И., Яркин В.В., Касимцев А.В. и др. // Физика и химия обработки материалов. 2006. №

15. С. 29 – 40.

16. Калита В.И., Комлев Д.И. Плазменные покрытия с нанокристаллической и аморфной структурой.

17. – М.: Лидер М, 2008. – 388 с.