Thermodynamic modeling of metal reduction in copper-smelting slags and experimental verification of its results

Over 110 million tons of slag were accumulated in the dumps of the Russian copper-smelting enterprises, and their number is increasing. Environmental taxes and dumps maintenance costs are burdensome, which makes it necessary to make the most complete disposal of these production wastes. At the same time, these slags contain valuable elements, in particular, iron, copper, zinc, selenium, arsenic and some others, the extraction of which can make recycling profitable. The paper presents the results of a thermodynamic calculation of the behavior of copper-smelting slag elements in the mixture with carbon during heating. Modeling was performed using the TERRA software package. The influence of the process temperature in the range of 600 – 1750 °C on reduction of iron, zinc and silicon was analyzed at the amount of carbon in the system corresponding to the stoichiometry of iron reduction reactions and exceeding the stoichiometric one. It was established that when heated above 650 °C, metallic iron appears in the system, and its full reduction is completed at 1250 °C. The appearance of metallic zinc is observed in two temperature ranges: in the first, appearance of zinc is observed with a simultaneous decrease in concentration of zinc oxide; in the second, an increase in concentration of metallic zinc with a simultaneous decrease in concentration of zinc sulfide. At temperatures above 1650 °C, silicon appears in the system. Under laboratory conditions, the processes of solid-phase reduction of iron with the capture of zinc oxide and separation of the reduction products were tested. It was established that as a result of pyrometallurgical separation by melting reduction products, iron-carbon alloys (steel and cast iron) and alloys with high silicon content can be obtained. The results of the work can be used in development of theoretical and technological foundations for the processing of copper smelting slags, which are not processed by existing technologies.

1. Sanakulov K.S., Khasanov A.S. Processing of Copper Production Slags. Tashkent: Fan, 2007, 238 p. (In Russ.).

2. Sabanova M.N., Orekhova N.N. Prospects for the use of flotation for processing environmentally hazardous stale copper-smelting slags. Gornyi informatsionno-analiticheskii byulleten’. 2017, no. 2, pp.  336–343. (In Russ.).

3. Sabanova M.N. Intensification of the copper slag flotation process in water circulation conditions: Extended Abstract of Cand. Sci. Diss. Moscow: 2016, 23 p. (In Russ.).

4. Lykasov A.A. Metallurgy of Non-Ferrous Metals. Chelyabinsk: South Ural State University, 2017, 197 p. (In Russ.).

5. ICSG, 2015: The World Copper Factbook 2015. International Copper Study Group. Lisbon-Portugal, 2015, 64 p.

6. Kho T.S., Swinbourne D.R., Lehner T. Cobalt distribution during copper matte smelting. Metallurgical and Materials Transactions B. 2006, vol. 37, no. 2, pp. 209–214. https://doi.org/10.1007/BF02693150

7. Chen C., Zhang L., Jahanshahi S. Thermodynamic modeling of arsenic in copper smelting processes. Metallurgical and Materials Transactions B. 2010, vol. 41, no. 6, pp. 1175–1185. https://doi.org/10.1007/s11663-010-9431-z

8. Bhavin Desaia, Vilas Tathavadkara, Somnath Basub, Kaushik Vakil. Behavior of selenium in copper smelting slag. In: Advances in Molten Slags, Fluxes, and Salts. Proceedings of the 10th Int. Conf. on Molten Slags, Fluxes and Salts. 2016, pp. 677–685.

9. Nadirov R., Syzdykova L., Zhussupova A. Copper smelter slag treatment by ammonia solution: Leaching process optimization. Journal of Central South University. 2017, vol. 24, no. 12, pp. 2799–2804. https://doi.org/10.1007/s11771-017-3694-3

10. Sukla L.B., Kar R.N., Panchanadikar V. Leaching of copper converter slag with Aspergillus niger culture filtrate. Biometals. 1992, vol. 5, no. 3, pp. 169–172. https://doi.org/10.1007/BF01061324

11. Muravyov M.I., Fomchenko N.V. Leaching of nonferrous metals from copper converter slag with application of acidophilic microorganisms. Applied Biochemistry and Microbiology. 2013, vol. 49, no.  6, pp. 562–569. https://doi.org/10.1134/S0003683813060136

12. Prince S., Young J., Ma G., Young C. Characterization and recovery of valuables from waste copper smelting slag. In: Advances in Molten Slags, Fluxes, and Salts: Proceedings of the 10th Int. Conf. on Molten Slags, Fluxes and Salts. 2016, pp. 889–898.

13. Sun S., Li H., Fan J., Li C., Liu Q. Recovery of cobalt from copper converter slag by reduction-sulfurization smelting at high temperature. In: 8th Int. Symp. on High-Temperature Metallurgical Processing. 2017, pp. 459–468.

14. Gonzalez C., Parra R., Klenovcanova A., Imris I., Sanchez M. Reduction of Chilean copper slags: a case of waste management pro­ject. Scandinavian Journal of Metallurgy. 2005, vol. 34, no. 2, pp.  143–149. https://doi.org/10.1111/j.1600-0692.2005.00740.x

15. Li K.Q., Ping S., Wang H.Y., Ni W. Recovery of iron from copper slag by deep reduction and magnetic beneficiation. International Journal of Minerals, Metallurgy, and Materials. 2013, vol. 20, no.  11, pp. 1035–1041. https://doi.org/10.1007/s12613-013-0831-3

16. Roshchin V.E., Potapov K.O. Selective reduction and pyrometallurgical extraction of iron from copper-smelting slags. Vestnik YuUrGU. Seriya “Metallurgiya”. 2014, no. 3 (14), pp. 25–29. (In Russ.).

17. Roshchin V.E., Roshchin A.V., Roshchin E.V. Method of selective extraction of metals from complex ores. Patent RF no. 2460813. Byulleten’ izobretenii. 2012, no. 25. (In Russ.).

18. Roshchin V.E., Roshchin A.V. Method of selective extraction of metals from complex ores formed by solid oxide solutions or oxide chemical compounds. Patent RF no. 2507277. Byulleten’ izobretenii. 2014, no. 5. (In Russ.).

19. Kosdauletov N., Roshchin V.E. Definition of conditions of selective iron reduction from iron-manganese ore. Izvestiya. Ferrous Metallurgy. 2020, vol. 63, no. 11-12, pp. 952–959. (In Russ.). https://doi.org/10.17073/0368-0797-2020-11-12-952-959

20. Kelamanov B., Samuratov Ye., Akuov A., Sariev O., Tastanova L., Abdirashit A. Thermodynamic-diagram analysis of Fe–Ni–C–O system. Metalurgija. 2022, vol. 61, no. 1, pp. 261–264.

21. Makhambetov Y., Timirbayeva N., Baisanov S., Baisanov A., Shabanov E. Thermodynamic modeling of phase composition for Fe–Ca–Si–Al system. Metalurgija. 2021, vol. 60, no. 1-2, pp. 117–120.

22. O’neill H.St.C. Quartz-fayalite-iron and quartz-fayalite-magnetite equilibria and the free energy of formation of fayalite and magnetite. American Mineralogist. 1987, vol. 72, no. 1-2,

23. pp.  67–75.

24. Salikhov S.P., Suleimen B., Roshchin V.E. Selective reduction of iron and phosphorus from oolite ore. Izvestiya. Ferrous Metallurgy. 2020, vol. 63, no. 7, pp. 560–567. https://doi.org/10.17073/0368-0797-2020-7-560-567