Effect of scrap using in charge on the microstructure and properties of ZhS6U nickel-based superalloy. Part 2. Structure analysis and mechanical properties of ZhS6U prepared with scrap

The second part of the article considers influence of the scrap amount on structure and mechanical properties of ZhS6U-VI nickelbased superalloy. As the use of scrap is associated with the possibility of alloy contamination by nonmetallic inclusions and loss of alloying elements, the influence of scrap on alloy structure and mechanical properties is in great importance. The samples with diameter of 12  mm were melted in a vacuum arc furnace and were casted into a copper mold from the virgin ZhS6U-VI alloy without scrap and from alloys with 50  % and 100  % of scrap. The alloys structures were investigated using optical microscopy on etched metallographic sections that were cut from the samples’ cross-sections. The studies were carried out on the as-cast samples and the samples after solution heat treatment for 4  hours at 1210  °C. The slightly higher nonmetallic inclusions content were observed in the structure of the alloy melted with scrap in comparison with virgin alloy melted without scrap. For the sample that was melted from 100  % of scrap the inclusions secure level is 3 (ASTM E 45-97) with an average size of inclusions of 28.4  ±  0.2  μm. Herewith the presence of single large inclusions with a size of not more than 70  microns was noted. However, it has no effect on the alloy mechanical properties. Mechanical properties after heat treatment (ultimate strength (UTS)  =  1090  –  1100  МPа and elongation (El)  =  9  –  11  %) were obtained on the samples melted using 50 and 100  % of scrap and fully correspond to the TU1-92-177-91 standard for ZhS6U-VI nickel-base superalloy. During solidification most of the large nonmetallic inclusions are concentrated under casting surface, which makes their machining difficult. Because of that the use of 100  % scrap without its preliminary processing is not recommended. Acceptable results were achieved when the 50  % of scrap was used.

1. Kablov E.N. Litye lopatki gazoturbinnykh dvigatelei: splavy, tekhnologiya, pokrytiya [Casted gas turbine blades: alloys, technology, coatings]. Moscow: Nauka, 2006, 632 p. (In Russ.).

2. Kishkin S.T., Stroganov G.B., Logunov A.V. Liteinye zharoprochnye splavy na nikelevoi osnove. Razrabotka i issledovaniya [Casting heat-resistant nickel-based superalloys. Development and research]. Moscow: Mashinostroenie, 1987, 116 p. (In Russ.).

3. Zelenyuk A.N., Naumik V.V., El’kin A.V. Using scrap in production of VZhL12E-VI alloy castings. Vіsnik Donbas’koi derzhavnoi mashinobudіvnoi akademii. 2011, no. 1 (22), pp. 198–202. (In Russ.).

4. Sidorov B.B., Rigin V.E., Kablov D.E. Organization of cast bar production from modern casting nickel-based superalloys. Liteinoe proizvodstvo. 2011, no. 10, pp. 2–6. (In Russ.).

5. Kablov E.N., Ospennikova O.G., Lomberg B.S. Strategic development directions of structural materials and technologies for their processing for aircraft nowadays and in future. Avtomaticheskaya svarka. 2013, no. 10–11, pp. 23–32. (In Russ.).

6. Binczyk F., Śleziona J., Mikuszewski T. Effect of repeated remelting on the chemical composition and structure of nickel alloys. Archives of foundry engineering. 2010, vol. 10, no. 1, pp. 189–194.

7. DeBarbadillo J.J. Nickel–base superalloys; physical metallurgy of recycling. Metallurgical Transactions A. 1983, vol. 14, no. 2, pp. 329–341.

8. Richards N.L., Chaturvedi M.C. Effect of minor elements on weld-ability of nickel base superalloys. International Materials Reviews. 2000, vol. 45, Issue 3, pp. 109–129.

9. Morscheiser J., Thönnessen L., Gehrmann B., Friedrich B. The influence of the slag composition on the desulfurization of Ni–based superalloys. Proceedings of the 2011 Int. Symposium on Liquid Metal Processing and Casting: Nancy, France. September 25-28, 2011. LMPC 2011, pp. 89–96.

10. Klochikhin V.V., Zhemanyuk P.D., Naumik V.V., Tsivirko E.I. Influence of solidification conditions on the quality of superalloys melted using foundry scrap. Liteinoe proizvodstvo. 2015, no. 6, pp. 2–5. (In Russ.).

11. Zelenyuk A.N., El’kin A.V., Naumik V.V. Investigation of the quality of weighted ingots, obtained using 100% of scrap refined by the method of temperature-time treatment. Novі materіali і tekhnologії v metalurgії ta mashinobuduvannі. 2012, no.1, pp. 45–48. (In Russ.).

12. Prasad V.S., Rao A.S., Prakash U.V., Rao R., Rao P.K., Gupt K.M. Recycling of superalloy scrap through electro slag remelting. ISIJ International. 1996, vol. 36, no. 12, pp. 1459–1464.

13. Kablov E.N., Ospennikova O.G., Sidorov V.V., Rigin V.E., Kablov D.E. Features of the modern melting and casting technology of cast heat-resistant nickel-based superalloys. Vestnik MGTU im. N.E. Baumana. Ser. Mashinostroenie. 2011, no. SP2, pp. 68–78. (In Russ.).

14. Zhang Z.W., Niu Y.J., Tian J.J., An N., Gao Y., Wang C., Shi S.F. The effect of remelting on the microstructure and mechanical properties of a nickel superalloy. Materials Science Forum. 2016, vol. 849, pp. 492–496.

15. Cheng J.–Q., Hu X.–J., Gu Y. Development and application of molds for producing large superalloy vacuum electrodes. Foundry. 2016, vol. 65, no. 9, pp. 917–919.

16. Koltygin A.V., Bazhenov V.E., Bazlov A.I., Bazlova T.A. Belov V.D. Effect of scrap using in charge on the structure and properties of ZhS6U nickel-based superalloy. Part 1. Microstructure analysis and phase composition of ZhS6U alloy prepared with scrap. Izvestiya. Ferrous Metallurgy. 2019, vol. 62, no. 5, pp. 360–365. (In Russ.).

17. Kovalenko V.S. Metallograficheskie reaktivy: Sprav. izd. [Metallographic etchants: Handbook]. Moscow: Metallurgiya, 1981, 120 p. (In Russ.).

18. Beckert M., Klemm H. Sposoby metallograficheskogo travleniya: Sprav. izd. [Methods of metallographic etching]. Trans. from Germ. Moscow: Metallurgiya, 1988, 398 p. (In Russ.).

19. Manjili M.H., Halali M. Removal of non–metallic inclusions from nickel base superalloys by electromagnetic levitation melting in a slag. Metallurgical and Materials Transactions B. 2018, vol. 49, no. 1, pp. 61–68.

20. Zhang T., Jiang J., Shollock B.A., Britton T.B., Dunne F.P.E. Slip localization and fatigue crack nucleation near a non–metallic inclusion in polycrystalline nickel–based superalloy. Materials Science and Engineering: A. 2015, vol. 641, August, pp. 328–339.

21. Baryshev E.E. , Kostina T.K., Tyagunov A.G., Savina L.G., Pavlinich S.P., Mysik R.K., Semenova I.P. Influence of high temperature treatment on structure of ZhS6U superalloy in liquid state and during solidification. Vysokotemperaturnye rasplavy. 1997, no. 1, pp. 26–31. (In Russ.).