blackmetИзвестия высших учебных заведений. Черная МеталлургияIzvestiya. Ferrous Metallurgy0368-07972410-2091National University of Science and Technology "MISIS"10.17073/0368-0797-2016-6-409-413blackmet-885Research ArticleМАТЕРИАЛОВЕДЕНИЕMATERIAL SCIENCEСПЕЦИАЛЬНЫЕ ГРАНИЦЫ В ПРОЦЕССЕ ВТОРИЧНОЙ РЕКРИСТАЛЛИЗАЦИИSPECIAL BORDERS IN THE SECONDARY RECRYSTALLIZATIONЛобановМ. Л.LobanovM. L.

д.т.н., профессор кафедры «Термообработка и физика металлов»

Dr. Sci. (Eng.), Professor of the Chair “Thermal Treatment and Physics of Metals”

m.l.lobanov@urfu.ruРусаковГ. М.RusakovG. M.

к.ф.-м..н., доцент кафедры «Термообработка и физика металлов», старший научный сотрудник

Cand. Sci. (Phys.-Math.), Senior Researcher, Assist. Professor Professor of the Chair “Thermal Treatment and Physics of Metals”

germanrusakov@yandex.ruРедикульцевА. А.Redikul’tsevA. A.

к.т.н., доцент кафедры «Термообработка и физика металлов»

Cand. Sci. (Eng.), Assist. Professor of the Chair “Thermal Treatment and Physics of Metals”

redikultsev@mail.ruКарабаналовМ. С.KarabanalovM. V.

к.т.н., доцент кафедры «Термообработка и физика металлов»

Cand. Sci. (Eng.), Assist. Professor of the Chair “Thermal Treatment and Physics of Metals”

m.s.karabanalov@urfu.ruЛобановаЛ. В.LobanovaL. V.

инженер кафедры «Термообработка и физика металлов»

Engineer of the Chair “Thermal Treatment and Physics of Metals”

m.l.lobanov@urfu.ruУральский федеральный университет имени первого Президента России Б.Н. Ельцина (620002, Россия, Екатеринбург, ул. Мира, 19)РоссияUral Federal University named after the first President of Russia B.N. Yeltsin, Ekaterinburg, RussiaRussian FederationУральский федеральный университет имени первого Президента России Б.Н. Ельцина (620002, Россия, Екатеринбург, ул. Мира, 19) Институт физики металлов УрО РАН (620219, Россия, Екатеринбург, ул. С. Ковалевской, 18)РоссияUral Federal University named after the first President of Russia B.N. Yeltsin, Ekaterinburg, Russia Institute of Metal Physics UB RAS (IMP UB RAS), Ekaterinburg, RussiaRussian Federation201604072016596409413Copyright © Лобанов М.Л., Русаков Г.М., Редикульцев А.А., Карабаналов М.С., Лобанова Л.В., 20162016Лобанов М.Л., Русаков Г.М., Редикульцев А.А., Карабаналов М.С., Лобанова Л.В.Lobanov M.L., Rusakov G.M., Redikul’tsev A.A., Karabanalov M.V., Lobanova L.V.Данная работа распространяется под лицензией Creative Commons Attribution 4.0.This work is licensed under a Creative Commons Attribution 4.0 License.https://fermet.misis.ru/jour/article/view/885

В исходном поликристаллическом сплаве Fe – 3 % Si методами ориентационной микроскопии (EBSD) исследованы различные стадии процесса низкотемпературного аномального роста зерен. На всех образцах была получена сравнительно низкая магнитная индукция В800 = 1,62 ÷ 1,72 Тл, соответствующая отклонению оси легкого намагничивания [001] кристаллитов от направления прокатки на угол 12 – 20°. Показано, что текстура вторичной рекристаллизации описывается ориентировками {110}<115>, мелкие зерна, находящиеся между аномально растущими кристаллитами (матрица вторичной рекристаллизации), имеют сильно рассеянную (близкую к аксиальной) текстуру {hkl}<001>. Показано, что ориентации выросших зерен близки к ориентациям, находящимся в разориентировке Σ5 к большинству кристаллитов, составляющих поглощаемую матрицу. Установлено, что аномально растущие зерна в последнюю очередь поглощают кристаллиты, имеющие с ними специальные границы Σ3 или Σ17b. 

In the initial polycrystalline alloy Fe – 3 % Si different stages of low-temperature abnormal grain growth have been studied using orientation microscopy techniques (EBSD). All the samples have been characterized by comparatively low magnetic induction В800 = 1.62 – 1.72 T, which corresponds to the axis deviation of easy magnetization [001] of crystals from the direction of rolling to the angle of 12 – 20°. It has been shown that the texture of the secondary recrystallization is described by the orientations {110 }<115>, small grains, situated among anomalously growing crystals (the matrix of the secondary recrystallization), have a heavily scattered (close to the axial one) texture {hkl}<001>. It is shown that the orientation of the grown grains is close to the orientations situated in misorientation Σ5 to most of the crystallites constituting the absorbed matrix. It has been found out that abnormally growing grains in the last turn absorb the crystallites having with them special Σ3 or Σ17b boundaries. 

сплав Fe – 3 % Siтекстурахолодная деформацияпервичная рекристаллизациявторичная рекристаллизацияспециальные границыalloy Fe – 3 % Sitexturecold deformationprimary recrystallizationsecondary recrystallizationspecial bordersReferencesTakahashi N., Harase J. Recent Development of Technology of Grain Oriented Silicon Steel // Proc. Mater. Science Forum. 1996. Vol. 204-206. Р. 143 – 145.Takahashi N., Harase J. Recent Development of Technology of Grain Oriented Silicon Steel. Proc. Mater. Science Forum. 1996, vol. 204-206, pp. 143–145.Günther K., Abbruzzese G., Fortunati S., Ligi G. Recent Technology Developments in the Production of Grain-oriented Electrical Steel // Steel research int. 2005. Vol. 76. No. 6. P. 413 – 421.Günther K., Abbruzzese G., Fortunati S., Ligi G. Recent Technology Develop-ments in the Production of Grain-oriented Electrical Steel. Steel research int. 2005, vol. 76, no. 6, pp. 413–421.Xia Z., Kang Y., Wang Q. Developments in the production of grainoriented electrical steel // Journal of Magnetism and Magnetic Materials. 2008. Vol. 254-255. Р. 307 – 314.Xia Z., Kang Y., Wang Q. Developments in the production of grainoriented electrical steel. Journal of Magnetism and Magnetic Materials. 2008, vol. 254-255, pp. 307–314.Lobanov M.L., Rusakov G.M., Redikul’tsev A.A. Electrotechnical anisotropic steel. Part I. History of development // Metal Science and Heat Treatment. 2011. Vol. 53. No. 7-8. P. 326 – 332.Lobanov M.L., Rusakov G.M., Redikul’tsev A.A. Electrotechnical anisotropic steel. Part. I. History of development. Metal Science and Heat Treatment. 2011, vol. 53, no. 7–8, pp. 326–332.Lobanov M.L., Rusakov G.M., Redikul’tsev A.A. Electrotechnical anisotropic steel. Part II. State-of-the-art // Metal Science and Heat Treatment. 2011. Vol. 53. No. 7-8. P. 355 – 359.Lobanov M.L., Rusakov G.M., Redikul’tsev A.A. Electrotechnical anisotropic steel. Part II. State-of-the-art. Metal Science and Heat Treatment. 2011, vol. 53, no. 7–8, pp. 355–359.Homma H., Hutchinson B. Orientation dependence of secondary recrystallization in silicon-iron // Acta Mater. 2003. Vol. 51. P. 3795 – 3805.Homma H., Hutchinson B. Orientation dependence of secondary recrystallization in silicon-iron. Acta Mater. 2003, vol. 51, pp. 3795–3805.Ko K-J., Rollett A. D., Hwang N.-M. Abnormal grain growth of Goss grains in Fe – 3 % Si steel driven by sub-boundary-enhanced solid-state wetting: Analysis by Monte Carlo simulation // Acta Materialia. 2010. Vol. 58. P. 4414 – 4423.Ko K-J., Rollett A. D., Hwang N.-M. Abnormal grain growth of Goss grains in Fe – 3 % Si steel driven by sub-boundary-enhanced solid-state wetting: Analysis by Monte Carlo simulation. Acta Materialia. 2010, vol. 58, pp. 4414–4423.Park H.-K., Kang J.-H., Park C.-S., Han C.-H., Hwang N.-M. Pancakeshaped growth of abnormally-growing Goss grains in Fe – 3 % Si steel approached by solid-state wetting // Materials Science and Engineering A. 2011. Vol. 528. Issues 7-8. P. 3228 – 3231.Park H.-K., Kang J.-H., Park C.-S., Han C.-H., Hwang N.-M. Pancake-shaped growth of abnormally-growing Goss grains in Fe – 3 % Si steel approached by solid-state wetting. Materials Science and Engineering A. 2011, vol. 528, Issues 7-8, pp. 3228–3231.Imamura T., Shingaki Y., Hayakawa Y. Effect of Cold Rolling Reduction Rate on Secondary Recrystallized Texture in 3 Pct Si – Fe Steel // Metallurgical and materials transactions A. 2013. Vol. 44A. No. 4. P. 1785 – 1792.Imamura T., Shingaki Y., Hayakawa Y. Effect of Cold Rolling Reduction Rate on Secondary Recrystallized Texture in 3 Pct Si – Fe Steel. Metallurgical and materials transactions A. 2013, vol. 44A, no. 4, pp. 1785–1792.Kumano T., Haratani T. and Ushigami Y. The Relationship between primary and secondary recrystallization texture of grain oriented silicon steel // ISIJ Int. 2002. Vol. 42. P. 440 – 449.Kumano T., Haratani T. and Ushigami Y. The Relationship between primary and secondary recrystallization texture of grain oriented silicon steel. ISIJ Int. 2002, vol. 42, pp. 440–449.Демаков С.Л., Водолазский Ф.В., Водолазский В.Ф., Попов А.А. Текстурное торможение рекристаллизации в титановом сплаве ТС6 // МиТОМ. 2010. No 10. С. 32 – 38.Demakov S.L., Vodolazskii F.V., Vodolazskii V.F., Popov A.A. Textural deceleration of recrystallization in titanium alloy TS6. Metal Science and Heat Treatment. 2011, vol. 52, no. 9–10, pp. 487–492.Shimizu R., Harase J. and Dingley D.J. Prediction of secondary recrystallization in Fe – 3 % Si by three-dimensional texture analysis // Acta Mater. 1990. Vol. 38. P. 973 – 978.Shimizu R., Harase J. and Dingley D.J. Prediction of secondary recrystallization in Fe – 3 % Si by three-dimensional texture analysis. Acta Mater. 1990, vol. 38, pp. 973–978.Redikul’tsev A.A., Lobanov M.L., Rusakov G.M. and Lobanova L.V. Secondary Recrystallization in Fe – 3 % Si Alloy with (110)[001] Single-Component Texture // The Physics of Metals and Metallography. 2013. Vol. 114. No. 1. P. 33 – 40.Redikul’tsev A.A., Lobanov M.L., Rusakov G.M. and Lobanova L.V. Secondary Recrystallization in Fe – 3 % Si Alloy with (110) [001] Single-Component Texture. The Physics of Metals and Metallography. 2013, vol. 114, no. 1, pp. 33–40.Homma H., Hutchinson B., Kubota T. The production mechanism of extensively sharp Goss orientation in HI-B material // Journal of Magnetism and Magnetic Materials. 2003. Vol. 254-255. P. 331 – 333.Homma H., Hutchinson B., Kubota T. The production mechanism of extensively sharp Goss orientation in HI-B material. Journal of Magnetism and Magnetic Materials. 2003, vol. 254–255, pp. 331–333.Грабский М.В. Структура границ зерен в металлах. – М.: Металлургия, 1976. – 160 с.Grabskii M.V. Struktura granits zeren v metallakh [Structure of grain boarders in metals]. Moscow: Metallurgiya, 1976, 160 p. (In Russ.).