blackmetИзвестия высших учебных заведений. Черная МеталлургияIzvestiya. Ferrous Metallurgy0368-07972410-2091National University of Science and Technology "MISIS"10.17073/0368-0797-2013-10-29-34blackmet-378Research ArticleЭКОЛОГИЯ И РАЦИОНАЛЬНОЕ ПРИРОДОПОЛЬЗОВАНИЕECOLOGY AND RATIONAL USE OF NATURAL RESOURCESОЦЕНКА МЕТАЛЛУРГИЧЕСКОЙ ЦЕННОСТИ КОНВЕРТЕРНОГО ШЛАКАTHE EVALUATION OF METALLURGICAL VALUE OF CONVERTER SLAGЗоряВ. Н.ZoryaV. N.ВолынкинаЕ. П.VolynkinaE. P.ПротопоповЕ. В.ProtopopovE. V.Сибирский государственный индустриальный университетRussian Federation20132803201556102934Copyright © Зоря В.Н., Волынкина Е.П., Протопопов Е.В., 20152015Зоря В.Н., Волынкина Е.П., Протопопов Е.В.Zorya V.N., Volynkina E.P., Protopopov E.V.Данная работа распространяется под лицензией Creative Commons Attribution 4.0.This work is licensed under a Creative Commons Attribution 4.0 License.https://fermet.misis.ru/jour/article/view/378

Проведены исследования характеристик и параметров конвертерного шлака ОАО «ЗСМК», в том числе с проведением серии экспериментальных плавок в лабораторной электродуговой печи. Установлено, что потери железа с конвертерным отвальным шлаком в условиях ОАО «ЗСМК» после первичной обработки на шлаковых полях путем отмагничивания магнитных компонентов составляют в среднем 22,7 %, в том числе 9,0 % в виде металлического железа и 13,7 % в составе оксидов. При сортировке шлака крупные фракции обогащаются оксидным железом, главным образом в виде (FeО) и (Fe3O4), в то время как (Fe2O3) переходит в мелкую фракцию. В процессе плавления конвертерного шлака происходит частичное восстановление железа, что сопровождается увеличением содержания металлического железа в среднем до 11,7 %. При этом основная доля металлического железа сосредоточена в крупных фракциях (более 40 мм) и составляет в среднем 18 %, в то время как в более мелких фракциях содержание металлического железа составляет 5 – 6 %.

The research of parameters of converter slag of JSC “ZSMK” was conducted, including the series of experimental smelting in a laboratory electric arc furnace. It was determined that the loss of iron with converter dump slag in JSC “ZSMK” after primary treatment on slag fields by removing of magnetic components is on the average 22.7 %, including 9,0 % in the form of metallic iron and 13,7 % in the oxides. In the process of sorting of slag the large fractions enrich themselves with oxide iron, mainly in the form of (FeO) and (Fe3O4), while the (Fe2O3) goes to the smaller fraction. In the process of melting of converter slag there is a partial recovery of iron, which is accompanied by an increase in the content of metallic iron in the average of 11,7 %. At the same time, the main part of the metallic iron is concentrated in large fractions (+40 mm) and is on the average of 18 %, while in the smaller fractions the content of the metallic iron is 5 – 6 %.

конвертерный шлакоксиды железасортировка шлакафракцияconverter slagiron oxideprocess of sorting slagfractionsReferencesКудрин В.А. Теория и технология производства стали. – М.: Мир, 2003. – 528 с.Кудрин В.А. Теория и технология производства стали. – М.: Мир, 2003. – 528 с.Юсфин Ю.С., Леонтьев Л.И., Черноусов П.И. Промышленность и окружающая среда. – М.: ИКЦ Академкнига, 2002. – 469 с.Юсфин Ю.С., Леонтьев Л.И., Черноусов П.И. Промышленность и окружающая среда. – М.: ИКЦ Академкнига, 2002. – 469 с.Рябов Т. В. // Новости черной металлургии за рубежом. 2000. № 4. С. 128 – 130; 2004. № 3. С. 75,76.Рябов Т. В. // Новости черной металлургии за рубежом. 2000. № 4. С. 128 – 130; 2004. № 3. С. 75,76.Голов Г. В. // Сталь. 1995. № 1. С. 73.Голов Г. В. // Сталь. 1995. № 1. С. 73.

The authors declare that there are no conflicts of interest present.